Abstract
Crystallinity, crystal structure and lamellar thickness in melt-crystallized samples of poly(propylene- stat-ethylene) fractions with 2.7–11.0 mol% ethylene comonomer and of approximately constant tacticity were assessed by wide- and small-angle X-ray scattering, differential scanning calorimetry and infra-red spectroscopy. Most of the samples were crystallized under isothermal conditions at 373 K. In comparison with an isotactic homopolymer of polypropylene, the copolymers showed lower crystallinity, melting enthalpy and average length of 3 1 helices, a slightly larger unit cell, a longer long period and an invariant lamellar thickness. The X-ray crystallinity of the copolymers remained approximately constant with increasing ethylene content, whereas the γ-crystallinity increased and the heat of fusion decreased moderately. It is suggested that the ethylene units are partially included in the crystals, and that this causes the invariance in crystallinity and crystal thickness. The observed gradual decrease in average 3 1 helix length with increasing ethylene content as assessed by infra-red spectroscopy is in accordance with this suggestion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.