Crystal structure and morphology of biaxially oriented polyamide 12 films

Abstract

AbstractThe structural and morphological characteristics of biaxially oriented polyamide 12 films are described on the basis of the results from differential scanning calorimetry, wide‐angle X‐ray diffraction (WAXD), polarized FT‐IR spectroscopy, and small angle X‐ray scattering (SAXS). The WAXD patterns of the oriented polyamide 12 films indicated only the monoclinic γ crystal with little dimensional changes of its unit cell depending on the stretching conditions. The crystallographic angles (α = γ = 90°, β = 121°) that were determined via the WAXD patterns confirmed the monoclinic symmetry of the γ crystal. Annealing the films stretched at 115 °C in boiling 20% formic acid solution did not result in structural changes of the crystalline unit cell. The chain‐axis repeat distance of 31.9 Å for the γ crystal was experimentally obtained with (0 26 0) planes. It was shortened as compared with that of all‐trans conformation. For films having primary orientation to MD, normals to the basal plane of folded‐chain lamellae were parallel to MD (primary stretch direction) resulting in two‐point SAXS patterns. Growth in long spacing with an increase of stretch temperature was discovered. Annealing the films induced further elongation in long spacing. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1189–1200, 2002