Abstract
The effects of indium impurity on the crystal structure and bonding characteristics of In-doped β-Zn4Sb3 were investigated by powder X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The XRD Rietveld refinement indicates that the indium impurity preferentially substitutes one of Sb atoms in Sb–Sb dimer at the 12c Sb(2) site and simultaneously leads to the increase of Zn occupancy. The observations of binding energy shift and a new valence state in Sb 3d core-level XPS spectra can be attributed to the charge transfer from In and Zn to Sb. As a result, more electropositive Zn atoms are needed to maintain the charge balance. The reduction of the lattice thermal conductivity is ascribed to the formation of the asymmetric Sb–In bond, resulting in much low lattice thermal conductivity of 0.49W−1K−1 of Zn4Sb2.96In0.04.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.