Crystal plasticity modelling and experiments for deriving microstructure-property relationships in γ-TiAl based alloys

Abstract

Single-crystals of γ-TiAl cannot be grown for the compositions present inside the two-phase γ/α2-microstructures that show good mechanical properties. Therefore the single crystal constitutive behaviour of γ-TiAl was studied by nanoindentation experiments in single phase regions of these microstructures. The experiments were extensively characterized by a combined experimental approach to clarify the orientation dependent mechanical response during nanoindentation. They further were analyzed by a three-dimensional crystal plasticity finite element model that incorporated the deformation behaviour of γ-TiAl. The spatially resolved activation of competing deformation mechanisms during indentation was used to assess their relative strengths. On the length-scale of multi-grain aggregates two kinds of microstructures were investigated. The lamellar microstructure was analyzed in terms of kinematic constraints perpendicular to densely spaced lamellar boundaries which lead to pronounced plastic anisotropy. Secondly, the mechanical behaviour of massively transformed microstructures was modelled by assuming a lower degree of kinematic constraints. This resulted in less plastic anisotropy on a single grain scale and lower compatibility stresses in a 64-grain aggregate. On the macroscopic length scale, the results could possibly explain the pre-yielding of lamellar microstructures.