Abstract
The oxygen exchange kinetics and the surface chemistry of epitaxially grown, dense La0.6Sr0.4CoO3-δ (LSC) thin films in three different orientations, (001), (110), and (111), were investigated by means of in situ impedance spectroscopy during pulsed laser deposition (i-PLD) and near-ambient-pressure X-ray photoelectron spectroscopy (NAP-XPS). i-PLD measurements showed that pristine LSC surfaces exhibit very fast surface exchange kinetics but revealed no significant differences between the specific orientations. However, as soon as the surfaces were in contact with acidic, gaseous impurities, such as S-containing compounds in nominally pure measurement atmospheres, NAP-XPS measurements revealed that the (001) orientation is substantially more susceptible to the formation of sulfate adsorbates and a concomitant performance decrease. This result is further substantiated by a stronger increase of the work function on (001)-oriented LSC surfaces upon sulfate adsorbate formation and by a faster performance degradation of these surfaces in ex situ measurement setups. This phenomenon has potentially gone unnoticed in the discussion of the interplay between the crystal orientation and the oxygen exchange kinetics and might have far-reaching implications for real solid oxide cell electrodes, where porous materials exhibit a wide variety of differently oriented and reconstructed surfaces.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.