Abstract
Crystals of the quaternary compounds α-Lu(Al1-xTx)B4(T = Fe, Cr) (YCrB4-type, orthorhombic, Pbam), obtained from the nominal composition of Lu(Al1-xTx)B3, were grown by using Al flux mixed with T metal at 1773 K for 5 h under an Ar atmosphere. The maximum dimensions and morphology of the crystals obtained were about 0.7 mm × 0.5 mm for flake-type crystals of Lu(Al1-xCrx)B4and about 5.2 mm × 0.2 mm for prism crystals of Lu(Al1-xFex)B4. The lattice constants determination and chemical analyses of Lu(Al1-xTx)B4(T = Fe, Cr) compounds were carried out for Fe 0.5 - 10.0 at% and Cr 0.5 - 1.0 at%. The lattice constants and the unit lattice volume in Lu(Al1-xTx)B4crystals decreased with increase of the concentration of Fe or Cr. The values of micro-Vickers hardness of Lu(Al1-xFex)B4(x = 0.005 - 0.030) and Lu(Al1-xCrx)B4(x = 0.005 - 0.010) samples are in the ranges of 16(2) - 20(3) GPa and 13(2) - 16(3) GPa, respectively. The hardness values showed a little increase as the solid solution of Fe or Cr was realized in Lu(Al1-xTx)B4, possibly because of distortion to the crystal structure. The magnetic susceptibility of as-grown Lu(Al0.995Fe0.005)B4crystals for example, exhibited diamagnetic behavior with a small ferromagnetic component.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.