Cryogenic reliability of composite insulation panels for liquefied natural gas (LNG) ships

Abstract

The major carrier of liquefied natural gas (LNG) is LNG ships, whose containment system is composed of dual barriers and composite insulation panels. The LNG containment system should have cryogenic reliability and high thermal insulation performance for safe and efficient transportation of LNG. The secondary barrier composed of adhesive bonded aluminum strips should keep tightness for 15 days, when the welded stainless primary barrier fails. However, cracks are generated in the composite insulation panels due to the local stress concentration and the brittleness of insulation materials at the cryogenic temperature of −163 °C. If cracks generated in the insulation panel propagate into the secondary barrier, LNG leakage problem might occur, which is a remaining concern in ship building industries. In this study, crack retardation capability in the composite insulation panel was investigated with glass fabric reinforcement. Finite element analysis was conducted to estimate the thermal stress at the cryogenic temperature and a new experimental method was developed to investigate the failure of secondary barrier of composite insulation panel. From the experimental results, it was found that the glass fabric reinforcement was effective to retard the crack propagation into the aluminum secondary barrier from the polyurethane insulation foam at the cryogenic temperature.