Abstract
Polyethylene-polyethylene blend films were prepared by gelation/crystallization from semidilute solution by using ultrahigh molecular-weight (mw) polyethylene (UHMWPE) (mw=6×106) and low molecular weight polyethylene (LMWPE) (mw=4×104). The UHMWPE/LMWPE compositions chosen were 50/50, 67/33, and 91/9. Elongation was carried out in a hot oven at 115–130°C. The drawn films were exposed to an electron beam under nitrogen flow. Radiation doses chosen were 10, 20, 40, and 100 Mrad. crosslinking caused a significant effect in improving high temperature resistance for the blend film with draw ratio of 20 in the case of irradiation doses less than 20 Mrad. The elongation beyond 20 times and high doses beyond 20 Mrad hampered the crosslinking effect and the specimens were easily torn manually. This is thought to be due to the fact that the excess irradiation dose causes main chain scission apart from crosslinking.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.