Abstract
Mixtures of Cr and Mo elemental powders, with the nominal compositions Cr25Mo75, Cr50Mo50, and Cr75Mo25, are processed by high-energy ball milling at ambient temperature. Milling is observed to force the mixing of the immiscible bcc elements Cr and Mo into solid solutions. The lattice parameter of these solid solutions, measured by X-ray diffraction (XRD), displays the expected positive deviation from Vegard’s law. These deviations are compared to the ones predicted by Eshelby’s inclusion model for dilute alloys. The conventional Williamson-Hall approach is shown to fail to determine the grain size in as-milled samples, probably due to the high density of dislocations. Annealing at 700 °C for 10 hours under argon leads to a large reduction in structural defect density, without inducing any significant decomposition. The mixing measured in Cr-Mo is discussed in the broader context of the mechanical mixing forced by ball milling in moderately immiscible systems.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.