Abstract
Abstract Cr-Mo diffusion layer on carbon steels was prepared by double glow plasma surface metallurgy and treated by ultra-saturated carbonization, quenching and tempering, the excellent wear resistance was obtained. The results indicated that the hardness of surface alloying was up to 1300 Hv 0.025 . The carbides in the alloyed layer were fine and dispersed without coarse eutectic ledeburite. The microstructure of the composite layer indicated that the dimension of surface carbides was less 1μm. The abrasion experimental results showed that the average relative wear resistance of modified-steels was 10.3 times as that of T10 steel by quenching and low tempering. The alloy layer possessed a very strong ability resistance to tempering, and its surface hardness exceeds 595 Hv 0.025 after tempering at 690°C for 4h.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.