Abstract
Strip-cast Al-1wt.%Mn-1wt.%Mg was subjected to thermomechanical treatment (TMT) in order to combine a dislocation substructure of submicron initial subgrain size L 0 with phase structures hardening, manganese either being participated or not. The influence of TMT on the mechanical properties was investigated between room temperature and 573 K by means of tests at a constant elongation rate and creep tests. The microstructure was investigated using transmission electron microscopy. TMT enhances the room temperature yield strength σ y according to σ y = σ 0 + kL 0 −1 where σ 0 and k are constants. At elevated temperatures the maximum strength is reached under most conditions after a small amount of strain (a few per cent). This is due to the microstructural changes that accompany deformation. The subgrain size changes during deformation from L 0 towards a steady state value L s , which in material which has no precipitated manganese is inversely proportional to stress. Under conditions where L s ∼ L 0, substructural hardening is prominent. However, for L s ⪢ L 0, there is virtually no hardening effect. Under intermediate conditions there is an initial strain range in which the specimen work hardens while the substructure coarsens. This is interpreted in terms of glide associated with recovery of the dislocation structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.