Abstract
High density La9.33Si6O26 polycrystals were fabricated by conventional and spark plasma sintering starting from nanopowders synthesized by freeze-drying. The materials exhibit a homogeneous microstructure formed by equiaxed grains with average sizes of 1.1 μm and 0.2 μm-diameter depending on the sintering route. Compressive mechanical tests were performed in air at constant strain rate between 900 and 1300 °C. A gradual brittle-to-ductile transition was found with increasing temperature and/or decreasing strain rate. Grain boundary sliding is the main deformation mechanism in the ductile region, characterized by a stress exponent n = 1 for the conventional sintered (large-grained) material and n = 2 for the spark plasma sintered (fine-grained) material; in both cases, the activation energy for creep was 360 kJ/mol. Effective cation diffusivities have been derived from mechanical data by comparison with appropriate models. The creep properties of lanthanum silicates are reported here for the first time.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.