Abstract
In the present paper, the creep behavior of sisal fiber cement based composites was investigated. The composites were manufactured using a matrix with low calcium hydroxide content, obtained by partially replacing the cement by fly ash and metakaolin. Two types of composites were developed, each with three layers of long and unidirectional sisal fibers, varying the condition of the fibers in saturated with water and with natural humidity. The mechanical behavior was evaluated through direct tension and four-point flexural tests. The composites reinforced with saturated fibers showed higher strain capacity in tension due to the properties of the fiber–matrix interface and lower ultimate bending strength. Cracking mechanisms were studied through photographs obtained during the tests, as well as analyzes by a stereoscopic microscope. All composites presented strain/deflection hardening behavior with the formation of multiple cracks. Tensile and flexural creep tests were performed on pre-cracked composites in order to study time-dependent responses. The evolution of cracks was monitored throughout the creep test with a stereoscopic microscope. The composites showed a reduction in strength and strain capacity after the creep tensile and flexural test, which resulted in a decrease in toughness of 36.9% and 48.5% for the composites with saturated fibers and natural humidity, respectively. In addition, for the flexural creep test, the composites with saturated fibers showed a decrease in toughness of 48.2% while the composite with natural humidity had a decrease of 35.3% for the load equivalent to 50% of their strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.