Abstract
The influence of interstitial strengthening and microstructure on creep deformation has been examined in the near-γ TiAl alloy Ti-48Al-lV-0.3C. Creep studies were conducted under constant load in air at 815 °C in the stress range of 50 to 200 MPa. Significant improvement in creep resistance was observed in this alloy compared with a similar alloy (Ti-49Al-lV) containing low levels of carbon (0.07 at. pct). The degree of strengthening resulting from the addition of carbon was found to be dependent on microstructure. At 815 °C and 150 MPa, the addition of carbon reduced the minimum creep rate by a factor of approximately 20 in the equiaxedy and duplex microstructures and by a factor of 3 in the fully lamellar microstructures. Carbide precipitation occurred in this alloy when aged in the temperature range of 700 °C to 950 °C. The addition of carbon leads to a decrease in the stress exponent from 4 to 3 in the duplex and equiaxedy microstructures and the inhibition of sub-boundary formation in the duplex microstructure. This suggests that solute/dislocation interaction mechanisms, rather than a direct effect of carbide precipitates, are responsible for the significant increase in creep resistance observed in this alloy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.