Abstract
By means of the method of the spark plasma sintering (SPS) on the basis of nanodimensional powder of nickel oxide (with an average particle size of about 100 nm), the fine-grained (of 250 – 500 nanometers approximately), dense (5.93 g/cm3), strong ceramics with the high microhardness Hv = 8.2 GPa, ultimate compressive strength ?B = 0.4 GPa and Young?s modulus of elasticity E = 140 GPa is created. The obtained ceramic sample was nickel oxide NiO (73-1519) with cubic structure, space group Fm3m (No. 225) and lattice size a = 4.168 ?.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.