Abstract
Abstract Single edge notched bars (SENB), in the bending mode, with a/W ratios ranging from 0.05 to 0.5 were examined for fracture toughness in terms of the J-integral approach. The results indicate that for a/W ratios less than 0.3, there is a significant loss of J-dominance. This loss is attributed to the effect of plastic deformation on the cracked face. For a/W ratios greater than 0.3, J-dominance is maintained into the large scale yielding regime. According to the recently developed two-parameter criterion (J,Q), compressive Q-stress was interpreted as an indication of low crack-tip stress triaxiality for shallow cracks, while positive Q-stress was associated with high crack-tip stress triaxiality for deep cracks. For the material properties and specimen geometries considered herein, a fracture toughness locus was constructed in terms of the (J,Q) parameters for each of the a/W ratios. The overall fracture data are in agreement with those predicted by other approaches and provide a rigorous framework for interpreting the effect of loss of crack-tip constraint in elastic-plastic fracture analyses.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.