Abstract
The root cause for cracking of rear brake components occurred during cold forming process was investigated. Optical micrographs showed the abundance of extended inclusions with several rounded ones in the steel. SEM image revealed the fracture surface which contained many extended cavities formed by extended inclusions and dimples all indicating a ductile rupture. EDS analysis confirmed that the extended inclusions were MnS type while the rounded ones were formed as a result of Ca-treatment. The crack propagation along with inclusions was clearly observed on the polished planes and on the fracture surface. It was determined that MnS type inclusions were the root cause for the cracking phenomena. The abundance of extended MnS inclusions indicated insufficient inclusion modification through Ca-treatment and insufficient removal of these inclusions in failed steel.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.