Bimetallic three-point-bending specimens and four-point-bending fatigue test specimens were produced from strength mismatched stainless steel/low carbon steel bi-material. Both the J resistance curves and fatigue crack growth behavior were investigated for the bi- and bulk materials. The results showed that a crack initiated easily at the interface, and crack growth resistance along interface was inferior to that of the corresponding bulk materials under either static or dynamic loading conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.