Crack propagation rate as a function of crack tip characteristics

Abstract

The dependence of crack growth rate on various crack tip parameters was studied. Experiments were performed on thin sheets of 6063-T6 Al-alloy having a central notch, to find crack tip opening displacement, total strain range, plastic strain range, crack opening stress and crack growth rate. Crack tip opening displacement and crack opening stress were measured, using a surface measurement technique, with small crack opening displacement gauges. The theoretical predictions of crack tip opening displacement compare fairly well with the experimental values. It is found that crack propagation rate vs total strain range-plastic strain range gives a straight-line fit on a log-log graph and, for positive stress ratios, the fatigue crack growth rates are found to be independent of R. Experimental results show that the crack opening stress is not affected by the position of the gauge when it is mounted behind and near the crack tip. The effect of mechanical properties and loading on crack growth were also studied. The specimens were fatigue cracked to a predetermined length and some specimens were annealed and again loaded cyclically. The application of cyclic loads to annealed specimens caused significant increase in crack propagation rates in comparison with the specimens having no heat-treatment. The load-displacement record was found to stabilize in about 10 cycles; the crack then extended slowly as a fatigue crack. Crack propagation rates for different values of R for annealed and work-hardened material were plotted against a crack tip parameter, ΔK∗, based on notional crack lengths. Since the results of d a d N vs ΔK∗ for both states of material (as-received and annealed) seem to lie on the same straight line on a log-log graph, the study provides a hope that the results for a material tested in any state (annealed or work-hardened) for positive values of R (0·0≤R≤0·3) will lie on this line, thus eliminating fatigue tests on the same material under different work-hardening conditions for different values of R. Models for d a d N have been developed using various crack tip parameters.