Abstract
AbstractStress corrosion cracking and corrosion fatigue of 12 Cr steel in sodium chloride solution has been investigated. Tests have been performed in air at room temperature and in aqueous solution with 22% NaCl at 80°C. The influence of corrosion pits on crack nucleation has been investigated. On fracture surfaces tested in environment (22% NaCl solution), crack initiation was observed in correspondence with corrosion pits; in this case fatigue life can be described using a fracture mechanics approach. The ΔK value for crack nucleation from a pit in rotating bending fatigue tests is very low in air (about 3 MPa√m). The results of slow strain rate tests on smooth specimens show that there is a threshold stress intensity, KISCC, of about 15 MPa√m and a plateau in stress corrosion crack growth rate of about 10‐5mm/s.