Abstract
We hypothesize that the fracture resistance of alumina core/porcelain veneer disks increases and that crack initiation shifts from veneer to core as the core/veneer thickness ratio (t(C)/t(V)) increases from 0.5/1.0 to 1.3/0.2, or as the elastic modulus of the supporting substrate (E(S)) to which it is resin-bonded increases from 5.1 to 226 GPa. When supported by a low-modulus substrate, disks with low t(C)/t(V) ratios exhibited cracks in the veneer and within the core, while those with high t(C)/t(V) ratios demonstrated core cracks, but not veneer cracks. None of the disks supported by Ni-Cr alloy (E = 226 GPa) exhibited core cracks. These results support the hypothesis that the crack initiation site shifts as the t(C)/t(V) ratio increases, but the increase in E(S) did not affect the crack initiation site. This study suggests that the t(C)/t(V) ratio is the dominant factor that controls the failure initiation site in bilayered ceramic disks.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.