Abstract
Crack healing in liquid-phase-pressureless-sintered SiC–AlN composites was investigated by introducing cracks into specimens and subsequently heat-treating the specimens. It was observed that cracks were healed and the strength was recovered. Cracks were filled with silica or mullite produced by the oxidation of the composites. It was shown that the healing temperature could be fixed in the range 1100–1300 °C and that large cracks up to about 300 μm could be healed completely. Our results imply that a simple oxidation heat-treatment can improve the reliability of silicon carbide–aluminum nitride components.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.