Abstract
The crack growth rate of two different constructed BGA resistor’s solder joint subjected thermal cycling was calculated using a dye penetration method. “ The crack percentage ” and the number of thermal cycling were recorded until the end of the test that “ the crack percentage” greater than 50%. 4-point cycling bending test was also performed to observe failure mode compared with thermal cycling. The experiment indicated that 1) The dyeing appearance of solder was central symmetry and 2)”The crack percentage” and the number of thermal cycling has the exponent relationship and 3)The crack happened on both PCB side and component side, the crack growth direction at component side is from outside to the component central and 4)the contrary crack growth direction was observed in the 4-point bending fatigue test and 5) the failure mode was proved by FEM.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.