Abstract
In this study the crack evolution and fracture toughness of HfO2/SiCN(O) ceramic nanocomposites were studied. These ceramics crack radially under indentation in contrast to Hertzian crack in SiOC ceramics. This difference was attributed to the variance in Poisson's ratio and elastic modulus to hardness ratio. Fracture toughness by crack opening displacement and radial crack length measurement was 0.8–1.2 MPa.m1/2 and 2.5–3 MPa.m1/2, respectively. The open network forming structure resulted in the over estimation of fracture toughness value by RCL.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.