Abstract
Isothermal fatigue testing was conducted on single crystal nickel-base superalloys. Distinct cracking behaviors were found to occur in the specimens treated by different laser shock processing (LSP) technologies. A crack generally initiates from the casting micropore. For the well surface strengthened specimens suffered high laser shock intensities, the crack initially grows along one or more of the {111} planes and falls on the edge of the cylindrical specimen. For the poorly strengthened specimens, the final fracture area is usually located inside.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.