Abstract
Different surface preparation processes and post-treatments were applied to ‘electroless’ E-coated AZ31B magnesium alloy. The corrosion performance of the differently treated samples was assessed by means of ASTM B117 salt spray, anodic polarisation curve and electrochemical impedance spectroscopy measurements respectively. The results show that the corrosion resistance of the ‘electroless’ E-coated AZ31B can be ranked in the following order: wet polishing+curing>dry polishing+curing≈wet polishing>dry polishing>commercial benchmark treatment. It suggests that a suitable pre- or post-treatment can significantly further improve the corrosion performance of an ‘electroless’ E-coated Mg alloy. The surfaces of the differently pre- and post-treated AZ31B were examined by SEM. It appears that the different corrosion resistances can be attributed to different microstructures of the surface films on AZ31B.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.