Abstract
AbstractIn this paper, a protective sealed Zn coating (SZC) was prepared on sintered NdFeB magnet by the combination of electrodeposition and sol–gel method. The unsealed Zn coating (UZC) was also studied for a comparison. The surface morphology of UZC and the cross‐section morphology of SZC were investigated using scanning election microscope (SEM). The microstructure of Zn coating and structure of sealing layer were studied by X‐ray diffraction (XRD) and Fourier transform infrared (FT‐IR) spectrum, respectively. The corrosion characteristics of SZC and UZC in neutral 3.5 wt% NaCl solution were evaluated using electrochemical measurements including open circuit potential (OCP), electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization test, indicating that the anticorrosive properties of SZC coated specimens increased 20 times compared with that of UZC coated specimens. In order to further investigate the anticorrosive properties of SZC, a long‐term immersion test was carried out in neutral 3.5 wt% NaCl solution using EIS. The results of long‐term corrosion test showed that the SZC could provide long‐term protection in neutral 3.5 wt% NaCl solution for NdFeB magnet.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.