Abstract
PurposeThe purpose of this paper is to investigate the effect of thermal treatment at low partial pressure of oxygen on electrochemical corrosion resistance of Ti‐47Al‐2Cr (at %) intermetallic, known as γ‐TiAl alloy.Design/methodology/approachThe surfaces of the samples were modified by thermal treatment at different temperatures in N2 gas flow for an hour. Characterization of the modified surface layers was carried out by microscopic examinations, hardness and roughness tests, and X‐ray diffraction analyses. Potentiodynamic polarization was used to evaluate the corrosion performance of γ‐TiAl in Ringer's solution.FindingsThe results indicated that the alloy treated at 950 °C had the optimum corrosion resistance, which can be attributed to the formation of an oxide layer by the surface thermal treatment and increase of the passive layer thickness.Practical implicationsLow corrosion rate (CR), high pitting potential (Epit), and more noble corrosion potential (Ecorr) make it possible for γ‐TiAl to be considered as a candidate for biomedical applications.Originality/valueThe treatment described in the paper is a novel method for surface modification of this type of alloy and results showed that it was an effective treatment and that the corrosion resistance improved remarkably.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.