Abstract
The corrosion properties of nickel silicide thin films are addressed by means of polarisation experiments in combination with X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) characterisation before and after the polarisation runs. The thin films studied included two pairs of nickel silicide of different compositions fabricated on Si wafer by means of ion-beam sputter deposition technique. For one pair, thin films were prepared by co-sputtering Si and Ni targets. To achieve higher crystallinity, the other pair was prepared by Ni sputter deposition followed by subsequent thermal annealing at 280 °C and 480 °C to develop single silicide phase of Ni 2Si and NiSi in individual film, respectively. The variation of the binding energy (BE) of Ni 2p 3/2 core-level peak in the XPS measurement in accordance with the Si content for this binary system follows a Boltzmann's relationship. The electrochemical polarisation tests conducted in 1.00 M HCl solution showed almost the same behaviour for the tested specimens irrespective of structure or film composition, still, the SEM and XPS studies together with optical microscopy showed that the Ni 2Si, leaner in Si, experienced thin film corrosion, whilst the NiSi appeared to be more resistant. Clearly, composition is found to be a more important design factor to tailor the corrosion properties than the structure for this binary silicide system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.