Abstract
High pressure and high temperature corrosion performance of high strength 15Cr martensitic stainless steel was studied in different severe environments—live acid (10% HCl + 1. 5% HF + 3% HAc + 5.1% corrosion inhibitor), spent acid and formation water containing CO2. The results show that the corrosion of high strength 15Cr martensitic stainless steel in live acid is most serious, and the uniform corrosion rate is far greater than those in spent acid and formation water containing CO2 corrosion environments, but all of them can be acceptable for oilfield. Acidizing corrosion inhibitor displays a good matching ability with the high strength 15Cr martensitic stainless steel in terms of decreasing the uniform corrosion rate, which changes mainly the anodic process of high strength 15Cr martensitic stainless steel. The corrosion potential moves to the positive direction, thus the corrosion current density decreases significantly. There arc some different degrees of pitting of high strength 15Cr martensitic stainless steel after corrosion tests in live acid, spent acid and formation water containing CO2, and the pitting density aggravates significantly and the maximum pit depth decreases in the corrosion sequence.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.