Abstract
Results of immersion tests of UNS N06625 (alloy 625), UNS S31609 (alloy 316 L), Ni–20Cr alloy and Nb coupons exposed to oxygenated ammoniacal sulphate solution at supercritical water oxidation (SCWO) conditions are presented. The corrosion behavior of the alloy 316 L (UNS S31603) SCWO reactor tubing is also presented under the same conditions. Immersion coupons corroded at a rate not exceeding 40 mm yr −1 while the reactor tube itself corroded at a rate of between 160–1500 mm yr −1, depending on which length of the reactor is considered to have corroded. Morphological and chemical analysis of the oxides present on the coupon samples suggest that iron oxides, which had initially precipitated on the corroding alloy 316 tube surface, were removed by heat flux-driven fluid mechanical action and transported through the reactor where they deposited on the coupons. Niobium was resistant to corrosion at the tested conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.