Abstract
The Al2O3-SiC-C or ASC castables are used in the main runners of blast furnaces. Most of the papers published to date focus on laboratory corrosion tests because access to the post-mortem samples of ASC castables is difficult. However, investigation of post-mortem samples is crucial in reducing the wear of ASC castables. The main runner is divided into the turbulence, middle, and non-turbulence zones. The microstructures of post-mortem samples located in working linings of different zones were investigated by SEM/EDS technique. The thermodynamic simulations were carried out in different systems, such as slag/refractory and iron/refractory, using the FactSage software. The SEM/EDS results showed the formation of phases with low melting points, such as gehlenite and anorthite, together with spinel solid solutions in the matrix and calcium dialuminate near the alumina aggregates. The thermodynamic simulations showed that slag and iron tend to react with alumina and silicon carbide, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.