Corrosion Inhibition of Medium Carbon Steel in the Acidic Medium Using Alcoholic and Aqueous Extract of Kujarat Tea Plant

Abstract

This study deals with the corrosion inhibition of metal corrosion process of medium carbon steel using 1M HCl for kinetic studies and rate reaction determination. The weight loss method is applied to pieces of Medium carbon steel divided to Cubans with dimensions (0.4*2*2.4) cm , and use Tafel Extrapolation Method, the samples were polished using carbide silicon paper with dimensions of (180,200,400,600,800,1000). The samples were immersed in the alcoholic medium ethanol at a temperature 293K for 3hr. Natural inhibitor Kujarat Tea (Hibiscus sabdarriffa L.) is used which is extracted in aqueous and alcoholic medium, different concentrations (1000،2000, 3000) ppm have been used ; The best concentration found through the results is a concentration found that is 1000 and 2000 ppm, the results indicate that the highest degree of inhibition for aqueous extract is 93.3% with the concentration of 2000 ppm and 90.5% with 1000 ppm at293K. While the alcoholic inhibitor shows the highest efficiency 92.4% with a concentration of 2000 ppm and 88.6% with a concentration of 1000 ppm respectively. The structure of the inhibitor was investigated using infrared spectroscopy (FTIR), and the surface morphology of the tested samples was investigated using a scanning electron microscope (SEM).