Abstract
The characteristics of corrosion-fatigue in age-hardened Al alloys, e.g. brittle striations on cleavage-like facets, are described, with reference to two examples of component failure. Mechanisms of corrosion fatigue (and explanations for fracture-surface features) are then reviewed. New observations of corrosion-fatigue crack growth for 7050-T7451 alloy compact-tension specimens tested in aqueous environments using a constant (intermediate) ΔK value but different cycle frequencies are then described and discussed. These observations provide additional support for a hydrogen-embrittlement process involving adsorption-induced dislocation-emission from crack tips.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.