Abstract
AbstractCorrosion fatigue behaviour and microstructural characterisation of G20Mn5QT cast steel are investigated in simulated seawater. Fractography is performed by using scanning electron microscopy (SEM). The macroscale fracture surface and microstructure of the failed specimen are acquired including the crack initiation, crack propagation, and pitting evolution. The maximum cyclic stress (S) versus number of cycles to failure (N) curves is derived by three‐parameter fatigue curve method. Fatigue life is predominantly controlled by the corrosion pitting‐induced crack initiation when tested in simulated seawater at lower stress levels. As the maximum cyclic stress is less than 185 MPa, the chloride ion erosion is the main influence factor, which affects the fatigue failure of the G20Mn5QT cast steel in simulated seawater.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.