Abstract
Abstract The corrosion fatigue behavior of FV520B steel in water and salt-spray environments at different temperatures is the focus of this study. Temperature has a significant effect on the fatigue behavior of FV520B steel in water and salt-spray environments, but has only a negligible effect in an air environment. Fatigue life decreases as temperature increases in water and salt-spray environments, and this trend is much more remarkable at a low stress amplitude level. As compared to air and water-spray, it was found that the chloride ion in salt-spray accelerated the fatigue damage of FV520B steel. Micro observation revealed that the fatigue cracks were initiated on the surfaces of the specimens in all experimental environments, and significant evidence of corrosion pits and micro cracks was found on the surfaces of the specimens in the salt-spray environment. Based on the pitting corrosion mechanism, a modified fatigue life prediction model that considered the combined effects of stress, temperature and corrosion was proposed. The study results show that the model predictions are in good agreement with the test data.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.