Abstract
The corrosion resistivity of single-phase Au-Cu-11 at% Pd alloys was evaluated by using a parameterQ which represented the total amount of anodic reaction in a potentiostatic polarization test. The result was compared with those for binary Au-Cu, ternary Au-Cu-11 at % Ag and some commercial alloys. The validity of usingQ as a corrosion parameter was confirmed by the good agreement between the analysed and calculated values of copper ion dissolved into the test solution. By replacing a part of the copper in Au-Cu alloys with palladium the corrosion resistivity can be greatly improved, but silver has no such significant effect. The value ofQ decreased by both treatments of homogenization and grain refinement of the alloy. One of the advantages of the alloy having a single-phase structure is that inhomogeneity in the distribution of the constituents is small even in the as-cast state, which results in a small galvanic effect.