Abstract
TiO2 films were deposited on AZ31 magnesium alloy substrates by r.f. magnetron sputtering. The corrosion behaviors in simulated body fluid (SBF) of the film samples were investigated and compared to the bare AZ31 magnesium alloy. After 3 days’ corrosion in SBF, only part of the TiO2 layer suffered from corrosion and the substrate was prevented from corrosion. In contrast, the bare magnesium alloy suffered from severe corrosion. After 10 days’ corrosion, the TiO2 layer was penetrated and the substrates still did not suffer from corrosion. After 15 days’ corrosion, besides TiO2 layer, the substrate suffered from corrosion to some degree. The depth of the corrosion layer is about 6 m, which is far lower than that of bare magnesium alloy, 40 m. The results show that TiO2 films effectively improve the corrosion properties of magnesium alloys.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.