Abstract
The corrosion behavior of X70 mild steel was investigated in the case of water deposited in CO2 pipeline by means of weight loss method and scanning electron microscopy (SEM). Results showed that general corrosion rate of X70 steel decreased with the increase of CO2 pressure from 4 to 12 MPa at 35 ℃. FeCO3 film and severe general corrosion was observed at 4 MPa, while thin and discontinuous corrosion product and serious pitting corrosion attack were found under other CO2 pressure conditions. It is of great corrosion risk to transport CO2 in gaseous or supercritical sta- tus for X70 mild steel if free water is formed in the pipeline.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Chinese Society of Corrosion and Protection
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.