Abstract
The corrosion resistance of Ti–25Nb–10Ta–1Zr–0.2Fe (mass fraction, %) (TNTZF) alloy in Ringer's solution at 37 °C was investigated by potentiodynamic polarization measurement. Ti–6Al–4V ELI (Extra low interstitial) alloy was also investigated to make a comparison. The results show that TNTZF alloy has higher corrosion potential, lower corrosion current density, more stable passive current density and wider passive region compared with Ti–6Al–4V ELI alloy, which indicates that TNTZF alloy has better corrosion resistance. In addition, pitting corrosion is observed on the surface passive film of Ti–6Al–4V ELI alloy but is not found on that of TNTZF alloy. The XPS analysis results reveal that the passive film formed on TNTZF alloy is composed of Nb2O5, NbO2, Ta2O5, ZrO2, TiO and Ti2O3 oxides in the matrix of TiO2, which makes the passive film more stable and protective than that formed on Ti–6Al–4V ELI alloy and contributes much to its superior corrosion resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.