Abstract
In this article, corrosion behavior of the single-layered TiN, single-layered CrN and multi-layered TiN/CrN coatings have been fabricated on 420C stainless steel (SS) by Cathodic Arc Evaporation (CAE) method in Ringer's solution was studied. The electrochemical appraisal was done by the Potentiodynamic Polarization (PDP) and Electrochemical Impedance Spectroscopy (EIS) tests. Results of PDP test revealed that all coated specimens have an increment in the polarization resistance (Rp) values (ranges from 438.2 to 593.6Ω.cm2) compared to bare SS (268.1Ω.cm2). Corrosion rate values for bare 420C SS and CrN, TiN and multi-layered TiN/CrN coatings were measured 0.086, 0.042, 0.050 and 0.068mpy, respectively. Furthermore, EIS results were showed that the single-layer CrN coating well depicted by an equivalent circuit with three time constants and has larger impedance and maximum logarithmic variation of C2. Finally, the corrosion performance results confirmed that single-layered CrN coating is an appropriate choice for deposition on 420C SS with the aim of application in general surgical instruments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.