Abstract
A series of the electrochemical and long-term corrosion tests was carried out in a 3.5 wt% Na2SO4 solution on thermal-sprayed WC-17Co and WC-10Co-4Cr cermet coatings in order to examine the effect of composition of binder materials on the corrosion behavior. The results reveal that the overall corrosion resistance of the WC-17Co coating is inferior to that of the WC–Co–Cr coatings due to the corrosion of binder materials which induce WC particles to fall off. CoO and WO3 oxide films form on the surface of WC-17Co coating in Na2SO4 solution electrochemical corrosion process, which will protect the coating in the process of corrosion. Cr2O3 oxide film formed on the WC-10Co-4Cr coating surface has a strong hindered role to corrosion. The corrosion mechanism of WC-17Co coating in Na2SO4 solution is entire corrosion of Co matrix, while it is film-hole corrosion mechanism for WC-10Co-4Cr coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.