Abstract
The results for the corrosion of alumina single crystals at 1700‐2000°C in argon, argon/water vapor, air, and air/water vapor for 10 h are reported. There were no obvious weight and volume changes after corrosion. White spots were observed on the surfaces of the specimens after corrosion tests. The initial temperature for the appearance of these white spots was 1800°C for argon and air, 1900°C for argon/water vapor, and 2000°C for air/water vapor. These white spots were likely formed by internal impurities, which diffused outward to the surface and coalesced at high temperatures. There was no evidence of corrosion damage inside the specimens. The flexural strength of the specimens was clearly enhanced after the corrosion tests and showed no evident relation to the corrosion conditions. This increase in strength after corrosion was likely due to the healing of surface machining flaws. The surface flaw healing temperature for alumina crystals was higher than 1400°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.