Abstract
The corrosion processes and mechanisms of Q235A steel under wet-dry cyclic condition were studied using polarization curve compared with immersion samples, while, the corrosion morphologies and corrosion products of the steel samples were characterized using scanning electron microscopy (SEM) and X-ray diffraction (XRD). The cathodic process of wet-dry samples was likely to be controlled not by the oxygen reduction, but rather by the reduction of corrosion products. During the drying process of the wet-dry sample, the electrolyte thickness decreased and chloride concentration increased. Oxygen would be much easier to diffuse into the interface of electrolyte/metal, which improved the cathodic reduction processes. Except for this, the rust itself took part in the reduction processes and hence increased the corrosion rate of the steel samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.