Abstract
Fe-based ferromagnetic [(Fe 1− x Ni x ) 0.75B 0.2Si 0.05] 96Nb 4 ( x = 0, 0.2 and 0.4) bulk glassy alloys (BGAs) with a diameter of 2 mm were prepared by copper mold casting. The corrosion behavior of glassy alloy rods obtained was investigated in 0.5 M NaCl, 0.5 M NaOH and 0.5 M H 2SO 4 aqueous electrolytes, respectively, using weight loss and electrochemical polarization measurements. It was found that the corrosion rates significantly decrease with an increase in Ni content in all examined solutions. The Ni-containing BGAs are spontaneously passivated with wide passive regions and low passive current densities in NaCl and NaOH solutions, but exhibit the active–passive–transpassive behavior in H 2SO 4 solution. The partial substitution of Ni for Fe results in a considerable improvement on the corrosion resistance of [(Fe 1− x Ni x ) 0.75B 0.2Si 0.05] 96Nb 4 BGAs, because of the structural and chemical homogeneousness of the amorphous phase and the effect of Ni on promoting the formation of a passive film. Besides their high glass-forming ability (GFA), excellent soft-magnetic properties and good mechanical performance, which have been reported before, these FeNi-based BGAs also feature rather high corrosion resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.