Abstract
The corrosion behavior of Cu–Al–Be shape memory alloys with different microstructures and Be content in a 3.5% NaCl solution was studied by weight loss, cyclic anodic polarization and chronoamperometric measurements. The beryllium has a beneficial effect in β alloys. A pitting potential of −100mV/SCE was found by anodic polarization tests for all the studied alloys, corresponding to the formation of pits produced by severe dealuminization. Samples with precipitates were more susceptible to pit formation. The corrosion behavior is strongly affected by the alloy microstructural conditions, and the β samples present higher pitting resistance and repassivation ability.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.