Abstract
The corrosion behavior and the relevant mechanism of carbon steels Q235 and Q450 exposed for 1 a in the hot and dry atmosphere environment at Turpan area was studied by weight lose test,scanning electron microscopy(SEM),energy dispersive spectra(EDS),X-ray diffraction(XRD) and stereological microscope.The results showed that the corrosion rate of carbon steel Q235 was greater than carbon steel Q450.The corrosion products on the surface of the carbon steels were consisted of α-FeOOH,γ-FeOOH and Fe3O4.The corrosion product of carbon steel Q235 was relatively loose for its rather low ratio of γ-FeOOH to α-FeOOH,whilst the corrosion product of carbon steel Q450 was dense for its higher ratio of γ-FeOOH to α-FeOOH.After removal of corrosion products,it could be observed that the depth and volume of corrosion pits of carbon steel Q235 was larger than those of carbon steel Q450.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.