Abstract

PurposeThis paper aims to study the effect of chloride ions concentration on the corrosion behavior of carbon steel in methyldiethanolamine (MDEA) aqueous solution in the sight of different process parameters of purification plant.Design/methodology/approachDue to the decrease of filtration efficiency and separation efficiency, the chloride ion in the desulfurization solution is enriched. The corrosion behavior of carbon steel under chloride ion enrichment environment was studied by weight-loss method, electrochemical impedance spectroscopy, cyclic polarization curve, X-ray photoelectron spectroscopy and scanning electron microscopy.FindingsThe results show that temperature and hydrogen sulfide loads are the main factors of corrosion in CO2-MDEA-H2O-H2S environment. The enrichment of chloride ions reduces the corrosion rate at low temperature but promotes the corrosion rate at high temperature. The chloride concentration should be controlled below 3000 mg/L, and no pitting corrosion was found under the experimental conditions.Originality/valueThe effect of chloride ion enrichment on MDEA solution corrosion shows that at low temperature, the increase of chloride ion will reduce the acid gas load and increase the density of corrosion products, so as to reduce the corrosion; on the contrary, at high temperature, the density of corrosion products will decrease and the corrosion will be intensified as well. It is believed that the chloride ion should be controlled below 3000 mg/L according to the results of the tests.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.