Abstract

The present work evaluates the effect of Co content on the microstructure and corrosion performance of Al-Co alloys of various compositions (2-32 wt% Co), fabricated by flux-assisted stir casting. A preliminary investigation on the effect of heat treatment (600 °C, up to 72 h) on the microstructure and corrosion behavior of Al-20 wt% Co and Al-32 wt% Co was also conducted. The Al- (2-10) wt% Co alloys were composed of acicular Al9Co2 particles uniformly dispersed in an Al matrix. The Al-20 wt% Co and Al-32 wt% Co alloys additionally contained Al13Co4 blades enveloped in Al9Co2 wedges. Heat treatment of Al-20 wt% Co and Al-32 wt% Co led to a significant reduction in the volume fraction of Al13Co4 and a decrease in hardness. Al-Co alloys with high Co content (10-32 wt% Co) exhibited greater resistance to localized corrosion in 3.5 wt% NaCl, but lower resistance to general corrosion compared to the (0-5 wt% Co) alloys. Heat treatment led to a slight increase in the corrosion resistance of the Al-Co alloys. The microstructure of the produced alloys was analyzed and correlated with the corrosion performance. Finally, corrosion mechanisms were formulated.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.