Abstract
Wrought aluminum sheets with thickness of 13mm were square butt-welded by friction stir welding (FSW) and gas tungsten arc welding (GTAW) methods. Corrosion behavior of the welding zone was probed by Tafel polarization curve. Optical metallography (OM) and scanning electron microscopy together with energy dispersive spectroscopy (SEM-EDS) were used to determine morphology and semi-quantitative analysis of the welded zone. FSW resulted in equiaxed grains of about 1–2μm, while GTAW caused dendritic structure of the welded region. Resistance to corrosion was greater for the FSW grains than the GTAW structure. In both cases, susceptibility to corrosion attack was greater in the welded region than the base metal section. T6 heat treatment resulted in shifting of the corrosion potential towards bigger positive values. This effect was stronger in the welded regions than the base metal section.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.